UV Curable Coatings DIABEAM™ for Lifestyle / Consumer Goods
DIABEAM™ UM series | Under / Top Coat for Metal Vapor Deposition
[閉じる]
DIABEAM™ UM series provides a strong bonding of the vapor deposition layer with ABS, PC, PET and PP while enhancing its appearance, heat and humidity resistance.
![](/en/products/departments/mcc/coating-mat/tech/__icsFiles/artimage/2023/03/27/cenmcc59_3/diabeam_consumer2en.jpg)
![](/en/products/departments/mcc/coating-mat/tech/__icsFiles/artimage/2023/03/27/cenmcc59_3/diabeam_consumer3.jpg)
MCC has over 40 years of innovation and experience in supplying coatings widely used for metal vapor deposition.
Grade | Suggested Applications |
Substrate | Recommended processing parameters | ||
---|---|---|---|---|---|
Thickness (Cured film) |
Solvent flash |
UV cure |
|||
UM-1007U | Cosmetic bottles such as skin lotions, mascaras and foundations, eyeliners, lipsticks, and blushes. Electrical appliance parts such as vacuum cleaners, washers, cameras, and smartphones. |
ABS Polycarbonate PMMA |
10-20μm | IR lamps: 1-2min. at 50-70℃* Forced air: 2-4min. at 50-70℃* |
Dose: 1000-2000mJ/cm2** Peak intensity: 100-200mW/cm2** |
UM-965U | PP | 10-20μm | IR lamps: 1-2min. at 50-70℃* Forced air: 2-4min. at 50-70℃* |
Dose: 1000-2000mJ/cm2** Peak intensity: 100-200mW/cm2** |
|
UM-875T | Aluminum deposition layer | 10-15μm | IR lamps: 1-2min. at 50-70℃* Forced air: 2-4min. at 50-70℃* |
Dose: 1000-2000mJ/cm2** Peak intensity: 100-200mW/cm2** |
*Substrate peak temp.
**Measured by EIT Power Puck II
DIABEAM™ MH series | Hard coat
[閉じる]
DIABEAM™ MH series bonds strongly onto plastic substrates enhancing its chemical, weather and abrasion resistance.
![](/en/products/departments/mcc/coating-mat/tech/__icsFiles/artimage/2023/03/27/cenmcc59_3/diabeam_consumer4en.jpg)
![](/en/products/departments/mcc/coating-mat/tech/__icsFiles/artimage/2023/03/27/cenmcc59_3/diabeam_consumer5.jpg)
MCC has over 40 years of innovation and experience in supplying coatings widely used in various fields.
Grade | Suggested Applications |
Substrate | Recommended processing parameters | ||
---|---|---|---|---|---|
Thickness (Cured film) |
Solvent flash | UV cure | |||
MH-4181 | Cosmetic bottles such as skin lotions, mascaras and foundations, eyeliners, lipsticks, and blushes. Electrical appliance parts such as vacuum cleaners, washers, cameras, and smartphones. |
ABS Polycarbonate |
10-15μm | IR lamps: 1-2min. at 50-70℃* Forced air: 2-4min. at 50-70℃* |
Dose: 1000-2000mJ/cm2** Peak intensity: 100-200mW/cm2** |
MH-4220 | PET | 10-15μm | IR lamps: 1-2min. at 50-70℃* Forced air: 2-4min. at 50-70℃* |
Dose: 1000-2000mJ/cm2** Peak intensity: 100-200mW/cm2** |
|
MH-4195 | PMMA | 10-15μm | IR lamps: 1-2min. at 50-70℃* Forced air: 2-4min. at 50-70℃* |
Dose: 1000-2000mJ/cm2** Peak intensity: 100-200mW/cm2** |
*Substrate peak temp.
**Measured by EIT Power Puck II
For further information (detailed conditions / typical results) or samples, please contact us.