ACRYKING™ is a coating that is cured by UV irradiation. Valued for its environmental friendliness, it is used for automotive headlamps.

Inquiries

ACRYKING™ | Weather-Resistant Hard Coats for Headlamps

[Close]

A thin, strongly bonded coating of ACRYKING™ on plastic substrate enhances the weatherability, scratch resistance and chemical resistance.

MCC has over 30 years of innovation and experience in supplying weather-resistant hard coats widely used for headlamps.

Grade Features Substrate Recommended processing parameters
Thickness
(Cured film)		 Solvent flash UV cure
PH-930 Excellent weatherability, high abrasion resistance, and good adhesion to PC substrate Polycarbonate 6-18μm IR lamps: 1-2min. at 60-80℃*
Forced air: 3-5min. at 60-80℃*		 Dose: 2500-6000mJ/cm2**
Peak intensity: 150-400mW/cm2**
PH-800N5A Very Good weatherability, high abrasion resistance, and good adhesion to PC substrate Polycarbonate 6-16μm IR lamps: 1-2min. at 60-80℃*
Forced air: 3-5min. at 60-80℃*		 Dose: 2500-7000mJ/cm2**
Peak intensity: 150-400mW/cm2**
F-328 Good weatherability, high abrasion resistance, and good adhesion to PC substrate Polycarbonate 6-10μm IR lamps: 1-3min. at 60-80℃*
Forced air: 3-5min. at 60-80℃*		 Dose: 3000-6000mJ/cm2**
Peak intensity: 150-400mW/cm2**

*Substrate peak temp.
**Measured by EIT Power Puck II

For further information (detailed conditions / typical results) or samples, please contact us.